Color variation of composite resins in relation to the Vita Classical shade guide: colorimetric analysis

Aim: The aim of this study was to verify the color variation between different composite resins and the Vita Classical Shade Guide. Methods: Two-millimeter thickness samples were made (n = 6) from eight commercial brands of composite resin (shade A2): Charisma (Kulzer), Forma (Ultradent), Harmonize (Kerr), Luna (SDI), Opallis (FGM), Oppus Bulk Fill (FGM), Vittra (FGM) and Filtek Z250 XT (3M ESPE). Specimens were stored in distilled water for 7 days and then polished. Color measurements of samples and A2 shade of the Vita Classical Shade Guide were performed using the Vita Easy Shade Advance 4.0 spectrophotometer on a black background. Color variations were calculated using the CIEDE2000 formula, considering values ≥0.81 being noticeable by the human eye and ≥1.77 being clinically unacceptable. Results were statistically analyzed with a 5% significance level. Results: Color variation (ΔE) of composite (E1 ) compared to the Vita Classical Shade Guide (E0 ) was greater than clinically acceptable for all the materials evaluated in this study. Forma (ΔE=2.08 ± sd=0.47) and Filtek Z250 XT (2.50 ± 0.20) had the smallest amount of color variation values found in the results. Harmonize (3.32 ± 0.63) presented values similar to Filtek Z250 XT, but it was worse than Forma. Vittra (3.51 ± 0.28), Charisma (3.80 ± 0.20), Opallis (4.24 ± 0.30) and Luna (5.67 ± 0.20) did not differ among each other and presented higher color variation than Forma, Filtek Z350XT and Harmonize. Oppus Bulk Fill (13.94 ± 1.12) was the composite with the greatest color variation. Conclusions: The findings in this study show that attention should be taken when using the Vita Color Shade Guide for composite shade selection

Efetividade da ozonioterapia contra microrganismos endopatogênicos: revisão de literatura / Effectiveness of ozone therapy against endopathogenic microorganisms: literature review

Introdução: A comunidade científica está em constante busca por alternativas terapêuticas que promovam a desinfecção dos canais radiculares. Dentre os diversos protocolos existentes, a terapia com o ozônio tem se mostrado uma técnica viável para tal finalidade. Assim, o objetivo da presente revisão de literatura é descrever a efetividade da ozonioterapia na redução de microrganismos endopatogênicos. Revisão de literatura e discussão: A literatura apresenta, em sua maioria, estudos laboratoriais e carece de estudos clínicos sobre o tema. Esses estudos demonstram que o ozônio líquido e gasoso possui propriedades antimicrobianas e é eficiente na desinfecção do sistema de canais radiculares. No entanto, devido aos diferentes protocolos de utilização da ozonioterapia, associado às diferenças metodológicas dos estudos, pode-se afirmar que a ozonioterapia parece ser eficiente na desinfecção dos canais radiculares, mas há controvérsias sobre a sua utilização como técnica complementar ou substituta às soluções irrigadoras tradicionais. Conclusão: Ainda não é possível afirmar que o ozônio pode ser um substituto ao hipoclorito de sódio. No entanto, alguns autores relatam que o ozônio pode ser utilizado como um agente coadjuvante na redução de microrganismos presentes nos canais radiculares e é uma alternativa viável para os casos em que o hipoclorito de sódio está contraindicado.

Introduction: The scientific community is in constant search for therapeutic alternatives that promote the disinfection of root canals. Among the various existing protocols, ozone therapy has been shown to be a viable technique for this purpose. Thus, the aim of the present literature review is to describe the effectiveness of ozone therapy on reduction of endopathogenic microorga-nisms. Literature review and discussion: Most part of the literature presents in vitro and clinical studies on the subject and demonstrate that the liquid and gaseous ozone have antimicrobial properties and are efficient in disinfecting the root canal system. However, due to the different protocols for ozone therapy use associated with the methodological differences from the studies, it can be indicated that ozone therapy seems to be an efficient disinfection of root canals, but there are controversies about its use as a complementary or substitute technique in place of traditional irrigation solutions. Conclusion:It is not yet possible to consider ozone as a substitute for hypochlorite sodium. However, some authors report that ozone can be used as a supporting agent on reduc-tion of microorganisms present in the root canals and a viable alternative for cases in which hypochlorite is contraindicated.

Effect of preheating on cytotoxicity and physicochemical properties of light-cured calcium-based cements / Efeito do pré-aquecimento na citotoxicidade e propriedades físico-químicas de cimentos à base de cálcio fotopolimerizáveis

ABSTRACT The aim of this study was to evaluate the degree of conversion, cytotoxicity, solubility and pH of photopolymerizable calciumbased cements submitted to preheating. The degree of conversion was analyzed by Fourier transform infrared, cytotoxicity by the MTT test and solubility through loss of mass. The data were subjected to statistical tests (ANOVA / Tukey's, p<0.05). The photopolymerizable materials showed a low degree of conversion, regardless of preheating. All materials caused a reduction in cell viability at 24 hours and 7 days, with the Dycal (control) being more cytotoxic. Heat had a positive effect on Biocal at 7 days. Dycal is the most soluble material. Heat had no effect on the solubility or pH of the polymerizable materials. It is concluded that photopolymerizable calcium-based cements have a low degree of conversion and are soluble, which results in mild to moderate cytotoxicity.

RESUMO O objetivo do presente estudo foi avaliar o grau de conversão, citotoxicidade, solubilidade e pH de cimentos à base de cálcio fotopolimerizáveis submetidos a pré-aquecimento. O grau de conversão foi analisado por espectroscopia no infravermelho com transformada de Fourier, a citotoxicidade pelo teste de MTT e a solubilidade através da perda de massa. Os dados foram submetidos a testes estatísticos (ANOVA/Tukey, p<0,05). Os materiais fotopolimerizáveis apresentaram baixo grau de conversão, independente do pré-aquecimento. Todos os materiais causaram redução da viabilidade celular nas análises de 24 horas e 7 dias, sendo que o Dycal (controle) apresentouse mais citotóxico e o calor apresentou efeito positivo sobre o Biocal na análise de 7 dias. O Dycal é o material mais solúvel e o calor não causou efeito na solubilidade e pH dos materiais polimerizáveis. Assim, conclui-se que os cimentos à base de cálcio fotopolimerizáveis apresentam baixo grau de conversão e são solúveis, que resulta em citotoxicidade suave e moderada.

O papel das mídias sociais na construção do conhecimento em Odontologia / The role of social media in the construction of knowledge in Dentistry

Este artigo, de cunho teórico, discute a construção do conhecimento em Odontologia no contexto da Sociedade em Rede, aproximando essa temática ao ponto de vista de alguns autores das Ciências Sociais Contemporâneas em voga. A bibliografia especializada aponta que a sociedade vive em uma constante transformação. Prova disso é que a construção de conhecimento pedagógico em Odontologia se dá hoje com maior intensidade na internet, principalmente nas mídias sociais, do que através da busca em livros. Por essa nova forma de agregar conhecimento ser uma realidade, é de fundamental importância que pessoas qualificadas sejam vetores de transmissão desses conhecimentos, de uma forma didática e com embasamento científico. Além disso, cabe aos professores se adaptarem ao novo estilo de construção do conhecimento pedagógico, elaborando aulas mais interativas e com o auxílio de ferramentas que chamem a atenção dos seus alunos e, concomitante a isso, ofereçam-lhes informações de qualidade.

This theoretical article discusses the construction of knowledge in dentistry in the context of the Network Society, bringing this theme closer to the point of view of some contemporary Social Science writers, nowadays in vogue. The specialized bibliography indicates that the society lives in a constant transformation, proof of this is that the construction of pedagogical knowledge in dentistry occurs today with greater intensity in the internet, mainly in the social media, than through the search in books. Because this new form of knowledge aggregation is a reality, it is of fundamental importance that qualified people are vectors of transmission of this knowledge, in a didactic and scientific basis. In addition, it is up to teachers to adapt to the new style of construction of pedagogical knowledge, developing more interactive classes and with the help of tools that attract the attention of their students and, at the same time, offer them quality information.